Self-Adaptation of Oxygen Adsorption and Sub-Surface Junction Formation in Thin Nanometric Sheets of Metal Oxides

Oxygen adsorption at metal oxide (MOX) surfaces and the formation of sub-surface depletion zones in thin nanometric sheets of MOX materials are theoretically investigated. It is shown that-under conditions of sufficient oxygen mobility-the bulk thermal generation of oxygen vacancy donors and the adsorption of surface oxygen ions cooperate in a self-organizing manner to form narrow sub-surface depletion zones which optimally fit into the limited spaces of MOX layers with nanometric cross sections. With this self-organization process in place, both the oxygen adsorption at free surfaces and the bulk generation of oxygen vacancy donors continuously increases as the MOX sheet thickness L is reduced, maintaining at the same time overall electro-neutrality and a state of perfect volume depletion of free carriers in bulk. This process comes to an end when MOX sheet thicknesses of L & AP; 1 nm are approached and when 3d-volumes of about 1 nm(3) contain only one single double-donor and two surface oxygen ions on average. It is argued that at this limit of miniaturization, different interpretations of MOX gas sensing phenomena might be required than on larger length scales.