Highly flame-retardant materials of different divalent metal ions alginate/silver phosphate: Synthesis, characterizations, and synergistic phosphorus-polymetallic effects

Three kinds of divalent metal ions (Ca2+, Cu2+, Zn2+) alginate/silver phosphate (MAlg/Ag3PO4) hybrid materials were prepared via an in-situ method, and the composites were characterized by X-ray diffractometry (XRD), Xray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and Fourier transform infrared spectrum (FTIR). To investigate their flame-retardant properties and phosphorus-polymetallic flame-retardant effects, the combustion behavior and flammability of the composites were assessed by using the thermogravimetric analysis (TGA), limiting oxygen index (LOI) and micro-calorimeter tests (MCC). The results show that the three composites were thermally stable, among which the LOI of CaAlg/Ag3PO4, CuAlg/Ag3PO4 and ZnAlg/ Ag3PO4 were 62.6 %, 46.5 % and 79.8 %, respectively, which were much higher than the prescribed flame retardants which was 27 %. According to the TGA, the thermal stability was ZnAlg/Ag3PO4 > CaAlg/Ag3PO4 > CuAlg/Ag3PO4. The heat release capacity (HRC) of the above three materials was 49 J/(g center dot K), 69 J/(g center dot K), 41 J/ (g center dot K), respectively, and the fire safety performance was also in the same order as the thermal stability. By using the thermogravimetric analysis coupled with Fourier transform infrared analysis (TG-FTIR) and pyrolysis-gas chromatography-mass spectrometry (Py-GC/MS), the flame retarding mechanism of MAlg/Ag3PO4 and the synergistic effect of Ag3PO4 and divalent metal ions were proposed based on the experimental data.