Effective corrosion inhibition of mild steel using novel 1,3,4-oxadiazole-pyridine hybrids: Synthesis, electrochemical, morphological, and computational insights.

An easy synthesis of two 1,3,4- Oxadiazole derivatives, namely, 2-phenyl-5-(pyridin-3-yl)-1,3,4-oxadiazole (POX) and 2-(4-methoxyphenyl)-5-(pyridin-3-yl)-1,3,4-oxadiazole (4-PMOX), and their corrosion-inhibition efficacy against mild steel corrosion in 1 N HCl, is evaluated using weight loss from 303 to 323 K, Electrochemical Impedance Spectroscopy (EIS), Potentiodynamic Polarization (PDP), Scanning Electron Microscopy (SEM), Energy Dispersive X-ray (EDX), UV-Vis spectroscopy, along with theoretical evaluation. Both POX and 4-PMOX exhibit excellent inhibition efficiency, with values reaching 97.83% and 98% at 500 ppm, respectively. The PDP analysis reveals that both derivatives act as mixed-type inhibitors. The Langmuir adsorption isotherm provides insights into the adsorption phenomena, demonstrating that 4-PMOX exhibits superior adsorption behavior on the mild steel surface compared to POX. This finding is further supported by SEM, DFT, RDF, and MSD analyses. Quantum mechanical parameters, including E, E, dipole moment (μ), energy gap (ΔE), etc., are in good agreement with the effectiveness of inhibition performance revealing ΔE values of 3.10 and 2.75 for POX and 4-PMOX, respectively. The results obtained from this study hold significant implications for researchers aiming to design more efficient organic inhibitors to combat metal corrosion.