Irradiation damage on CrNbTaVWx high entropy alloys

R. Martins,J.B. Correia, P. Czarkowski,R. Miklaszewski,A. Malaquias, R. Mateus, E. Alves,M. Dias

Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms（2023）

引用 0|浏览2

暂无评分

摘要

•The irradiated sample with higher W content shows swelling and melting for all discharges, the CrNbTaVW only shows blisters.•The effect of irradiation was more severe in CrNbTaVW1.7 when compared to CrNbTaVW.•The deuterium retention was evidenced to be in a deeper depth between 1.3 and 3 μm.•Deuterium retention was higher for CrNbTaVW1.7 when compared with CrNbTaVW for 3 discharges applied.

查看译文

关键词

Plasma facing components,High entropy alloys,Irradiation damage,Melting,Swelling