Ultrafine-grained Al-La-Mg-Mn alloy with superior thermal stability and strength-ductility synergy
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING(2023)
摘要
Ultrafine-grained (UFG) structures are highly desirable in microstructural design for their substantial improve-ments in strength and ductility; however, they often face challenges such as thermal instability and high manufacturing costs. In this work, powder hot-extrusion was employed as a cost-effective method to fabricate an Al-La-Mg-Mn alloy with a UFG structure (-0.8 mu m). The as-fabricated alloy exhibited a high-volume fraction of bimodal sub-micron intermetallics, with coarse intermetallics (-270 nm) distributed primarily along the grain boundaries and fine ones (<80 nm) in the grain interior. This unique structure cooperatively retarded the grain growth, resulting in a UFG structure with excellent thermal stability. The grain size grew slightly to 1.08 mu m after thermal exposure at 400 C for 100 h. Moreover, the UFG structure exhibited an excellent combination of strength and ductility, with yield strength, ultimate tensile strength, and elongation of 365 MPa, 543 MPa, and 13%, respectively. The UFG structure, decorated with bimodally distributed intermetallics, presents a promising microstructural design for UFG-structured alloys with excellent thermal stability and mechanical properties.
更多查看译文
关键词
al–la–mg–mn alloy,ultrafine-grained,strength-ductility
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要