Evaluation of Physical Properties and Material Characterization for Structural Frame at the Stained Glass Windows to Gongju Jeil Church of the Registered Cultural Heritage in Korea

The Christian Museum of Gongju Jeil Church was first built in 1931 and was largely damaged during the Korean War, but the walls and chimneys have been preserved. This building has a high architectural values in that the chapel was reconstructed in 1956, and maintains its original form through repair of damaged parts rather than new construction. The stained glass windows were as installed in 1979 and has a great significance in the Dalle de Verre method using lump glass. However, some of the stained glass damaged partially, such as various cracks and splits, and vertical and horizontal cracks in the joint fillers of supporting the colored glass. As the structural materials of the stained glass window, an iron frame and cement mortar filled with it were used, and corrosion of iron, cracking of mortar and granular decomposition appear partially due to weathering. In the joint fillers, the content of Ca and S is very high, indicating that gypsum were used as admixtures, and the gypsums grow in a rhombohedral and forms a bundle, which is investigated to have undergone recrystallization. As a result of modeling the ultrasonic velocity at the joint fillers, the left and right windows at the entrance show relatively weak in the range of 800 to 1,600m/s, and the lower right corner of the altar window and the upper left corner of the center window were also 1,000 to 1,800m/s, showing relatively low physical properties. And gypsums produced during the neutralization of lime mortar were detected in the joint fillers and contaminants on the surface. Such salts may cause damage to the joint material due to freezing and thawing, so appropriate preventive conservation is required. Also, since various damage types are complexly appearing in stained glass window and joint filler, customized conservation treatment should be reviewed through clinical tests.