SnLa2O5 wrapped carboxymethyl cellulose mixed calcium alginate nanocomposite beads for efficient reduction of pollutants

In this project, lanthanum oxide doped tin oxide (SnLa2O5) nanomaterial was prepared and characterized morphologically and physiochemically by different techniques. The catalytic performance of SnLa2O5 was assessed toward catalytic reduction of 4-nitrophenol (4-NP), methyl orange (MO), congo red (CR), methylene blue (MB) and potassium ferricyanide (K3[Fe(CN)6]). SnLa2O5 was found to be efficient for K3[Fe(CN)6] in the presence of NaBH4, which reduced in only 8.0 min. SnLa2O5 was further wrapped in carboxymethyl cellulose mixed calcium alginate (CMC-Alg) hydrogel beads because the powder catalyst cannot be simply recovered from reaction media to recycle and use again. SnLa2O5 wrapped CMC-Alg (SnLa2O5/CMC-Alg) was assessed for detail analysis of K3[Fe(CN)6] reduction. The effect of NaBH4, K3[Fe(CN)6] concentration and amount of catalyst was optimized using SnLa2O5/CMC-Alg. The amount of catalyst has positive impact on catalytic reduction of K3[Fe (CN)6]. The kinetic study revealed that K3[Fe(CN)6] reduction by SnLa2O5 and SnLa2O5/CMC-Alg was fast, which completed in 8.0 and 4.0 min with rate constant of 0.4283 min-1 and 0.7461 min-1, respectively. These findings indicated that the developed SnLa2O5/CMC-Alg is best and proficient nanocatalyst for K3[Fe(CN)6] reduction. The efficiency along with cost-effective and simple treatment route of the developed nanocatalyst have prospect to compete and replace the reputable commercial catalysts.