Effects of Re and Co additions on lattice parameters and lattice misfit in cast Ni-based superalloys

Morphological evolution of gamma prime precipitates was governed by an elemental partitioning ratio between the gamma and gamma prime phases. In the present study, Ni-based MGA 1400 alloy was modified by adding 4 wt% of Re and 6.4 wt% of Co by vacuum arc melting. The effects of Re and Co additions on lattice parameters of gamma and gamma prime phases were studied by TEM and XRD techniques. Calculated lattice misfit values obtained from XRD and TEM techniques were used to identify the shape and morphology of gamma prime precipitated particles after long-term exposure at 1173 K for 1800 ks? After long-term exposure, gamma prime particles became much coarser. The addition of Re retarded the coarsening rate of the gamma prime precipitates, resulting in smaller gamma prime particles at the same annealing times. Even though, both Re and Co atoms are strongly partitioned in the gamma matrix, the effect of Re and Co additions on lattice misfits was contradictory. The addition of Re produced rounded corner cuboidal morphology of gamma prime precipitates due to higher magnitude with negative lattice misfit (-0.3857%), while Co addition provided a more rounded shape of gamma prime particles due to the lattice misfit value approach to zero (+0.0936%).