Bridgman Growth of New Nonlinear Optical Crystal (La_{1 − x}Sm_x)₃Ga_5.5Nb_0.5O₁₄ for Quasi-Parametric Chirped Pulse Amplification

Samarium-doped La3Nb0.5Ga5.5O14 (Sm:LGN) crystals were grown along a (100)-orientation by the Bridgman method for quasi-parametric chirped pulse amplification (QPCPA) applications. The structure of La1-xSxmGN (x = 0.1, 0.2) crystals was the same as that of La3Nb0.5Ga5.5O14 (LGN) crystals. The effective segregation coefficient of Sm3+ in the La0.9Sm0.1GN crystal was 0.140. The full width at half maximum (FWHM) of La1-xSxmGN (x = 0.1,0.2) crystals was lower than 50″, which indicated the high quality of the crystals. The density of the La0.9Sm0.1GN crystal was 5.968 g/cm3 and that of the La0.8Sm0.2GNcrystal was 5.988 g/cm3. The transmittance of the crystals at 532nm and 800nm was all above 73%. The absorption spectra indicated that the crystals had strong absorption peaks at wavelengths of 1544 and 1595 nm. The thermal properties of La1-xSxmGN (x = 0.1, 0.2) crystals were similar to those of the LGN crystals. The laser damage thresholds of La0.9Sm0.1GN and La0.8Sm0.2GN crystals were, respectively, 188.30 and 54.84 TW/cm2 (@800 nm,35 fs).