Synthesis of High Quality Transparent Nanocrystalline Diamond Films on Glass Substrates Using a Distributed Antenna Array Microwave System

Diamond is a material of choice for the fabrication of optical windows and for protective and anti-reflecting coatings for optical materials. For these kinds of applications, the diamond coating must have a high purity and a low surface roughness to guarantee a high transparency. It should also be synthesized at low surface temperature to allow the deposition on low melting-point substrates such as glasses. In this work, the ability of a Distributed Antenna Array (DAA) microwave system operating at low temperature and low pressure in H-2/CH4/CO2 gas mixture to synthesize nanocrystalline diamond (NCD) films on borosilicate and soda-lime glass substrates is investigated aiming at optical applications. The influence of the substrate temperature and deposition time on the film microstructure and optical properties is examined. The best film properties are obtained for a substrate temperature below 300 degrees C. In these conditions, the growth rate is around 50 nm center dot h(-1) and the films are homogeneous and formed of spherical aggregates composed of nanocrystalline diamond grains of 12 nm in size. The resulting surface roughness is then very low, typically below 10 nm, and the diamond fraction is higher than 80%. This leads to a high transmittance of the NCD/glass systems, above 75%, and to a low absorption coefficient of the NCD film below 10(3) cm(-1) in the visible range. The resulting optical band gap is estimated at 3.55 eV. The wettability of the surface evolves from a hydrophilic regime on the bare glass substrates to a more hydrophobic regime after NCD deposition, as assessed by the increase of the measured contact angle from less than 55 degrees to 76 degrees after the deposition of 100 nm thick NCD film. This study emphasizes that such transparent diamond films deposited at low surface temperature on glass substrate using the DAA microwave technology can find applications for optical devices.