Rapid Gas-Phase Synthesis of the Perovskite-Type BaCe0.7Zr0.1Y0.1Yb0.1O3-delta Proton-Conducting Nanocrystalline Electrolyte for Intermediate-Temperature Solid Oxide Fuel Cells

ACS APPLIED MATERIALS & INTERFACES

引用 2|浏览1
暂无评分
摘要
Perovskite-type proton-conducting materials, such as BaCe0.7Zr0.1Y0.1Yb0.1O3-delta (BCZYYb), are very attractive for the next generation equipment of electrochemical energy conversion and storage owing to their excellent conductivity in the intermediate-temperature range (300-750 degrees C), as well as good thermo-chemical stability, coking resistance, and sulfur tolerance. However, the lack of a reliable and costeffective synthesis method for such multi-component co-doping oxides limits their large-scale application. In this study, for the first time, we successfully synthesize BCZYYb electrolyte nanopowders by using a rapid, scalable flame-based gas-phase synthesis method with two different barium precursors Ba(NO3)2 and Ba(CH3COO)2, named as BCZYYb (N) and BCZYYb (CA). The as-synthesized nanoparticles exhibit good crystallinity of the pure orthorhombic perovskite BCZYYb phase. BCZYYb (CA) shows more uniform doping with the element ratio of 1:0.74:0.12:0.08:0.1, which is very close to the theoretical value. The shrinkage and surface SEM (scanning electron microscope) results indicate that the flame-made powders have superior sinterability compared to the sol-gel-made powders because of the smaller primary particle size (-,20 nm). Electrochemical impedance spectroscopy tests show that BCZYYb (CA) sintered at 1450 degrees C has the highest protonic conductivity of 1.31 x 10-2 S cm-1 in wet H2 when operating at 600 degrees C and still maintains a high-level conductivity of 1.19 x 10-2 S cm-1 even when the sintering temperature is reduced to 1350 degrees C, which is mainly attributed to uniform doping and good sinterability. The activation energy for the conductivity of BCZYYb (CA) is also significantly lower than that of conventional electrolytes, which suggests much better conductivity in the intermediate (-,600 degrees C) and even lower operating temperature. The excellent conductivity performance combined with the high-throughput production capability makes the swirling spray flame a promising synthesis method for promoting the BCZYYb electrolytes from lab to industrial-scale solid oxide fuel cells.
更多
查看译文
关键词
nanocrystalline BCZYYb proton-conducting electrolyte, spray flame synthesis, sintering behavior, protonic conductivity, intermediate-temperature SOFCs
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要