Highly Thermal Conductive and Electrically Insulating Epoxy Composites Based on Zinc-Oxide-Coated Silver Nanowires

Nano-ZnO particles were deposited on the surface of silver nanowires (AgNWs) by the precipitation method, and the obtained AgNW@ZnO filler with core-shell structure was added to epoxy resin to prepare AgNW@ZnO/EP thermally conductive composites. The ZnO coating on the surface of AgNWs effectively improves the thermal conductivity of the composites. When 8 wt% AgNW@ZnO filler was added to the epoxy resin, the thermal conductivity of the AgNW@ZnO/EP composite increased to 0.77 W/(m center dot K). The enhancement of the thermal conductivity is attributed to the fact that ZnO effectively improves the interface bonding between AgNWs and the epoxy matrix, thus strengthening the contact between AgNWs. In addition, the electrical insulation of the AgNW@ZnO/EP composites was improved upon the introduction of the ZnO coating over AgNWs. For the filler content of 8 wt%, the volume resistivity of the AgNW@ZnO/EP composites was found to be higher than 10(13) omega center dot cm. AgNW@ZnO/EP composites have also exhibited low dielectric constant and good thermal stability.