The corrosion characteristic and mechanism of Mg-5Y-1.5Nd-xZn-0.5Zr ( x = 0, 2, 4, 6 wt.%) alloys in marine atmospheric environment

The microstructure and precipitated phases of as -cast Mg-5Y-1.5Nd-xZn-0.5Zr ( x = 0, 2, 4, 6 wt.%) alloys were investigated by optical microscopy, scanning electron microscopy, energy -dispersive spectrometry and X-ray Diffraction. The exposure corrosion experiment of these magnesium alloys was tested in South China Sea and KEXUE vessel atmospheric environment. The corrosion characteristic and mechanism of magnesium alloys of Mg-5Y-1.5Nd-xZn-0.5Zr ( x = 0, 2, 4, 6 wt.%) alloys were analyzed by weight loss rate, corrosion depth, corrosion products and corrosion morphologies. The electrochemical corrosion tests were also measured in the natural seawater. The comprehensive results showed that Mg-5Y-1.5Nd-4Zn-0.5Zr magnesium alloy existed the best corrosion resistance whether in the marine atmospheric environment and natural seawater environment. That depended on the microstructure, type and distribution of precipitated phases in Mg-5Y-1.5Nd-4Zn-0.5Zr magnesium alloy. Sufficient quantity anodic precipitated phases in the microstructure of Mg-5Y-1.5Nd-4Zn-0.5Zr alloy played the key role in the corrosion resistance. (c) 2022 Chongqing University. Publishing services provided by Elsevier B.V. on behalf of KeAi Communications Co. Ltd. This is an open access article under the CC BY -NC -ND license ( http://creativecommons.org/licenses/by-nc-nd/4.0/ ) Peer review under responsibility of Chongqing University