Transfer film growth of continuous carbon fiber reinforced thermoplastic poly(ether ether ketone) facilitated by surface texture during dry sliding
JOURNAL OF MATERIALS SCIENCE(2022)
摘要
To show the effect of surface texture on transfer film growth of continuous carbon fiber-reinforced thermoplastic poly(ether ether ketone) (CCF-PEEK), tribological behaviors of untextured and laser-engraved-dimple-textured WC–Co, TiN and DLC surfaces dry-sliding against CCF-PEEK pin were studied in ambient atmosphere ( pv = 0.46 MPa•m/s). Little tribo-film formed on untextured WC–Co, TiN and DLC, but continuous, relatively uniform CCF-PEEK transfer films with micron-level thickness grew from the majority of dimples along the sliding direction on textured WC–Co, TiN and DLC. A stable reduction in coefficient of friction by nearly 38.3% was achieved by textured WC–Co compared to the untextured. Texturing also yielded significant friction reduction to TiN, but almost did not lower the friction of DLC. Micro-cutting effect from the dimple texture edges probably caused considerable material removal of the counterpart CCF-PEEK pin and the repetitive friction cycles shaped the CCF-PEEK wear debris into the tribo-films. The friction reduction could be primarily attributed to the substantial mediation of tribological CCF-PEEK transfer films on the sliding interface. This study indicates that surface texture can facilitate the growth of polymeric transfer films with tribological application potentials in dry-sliding conditions.
更多查看译文
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要