A Nonionic Alcohol Soluble Polymer Cathode Interlayer Enables Efficient Organic and Perovskite Solar Cells

The choice of interfacial materials and their properties play a critical role in determining solar cell performance and stability. For compatibility with roll-to-roll printing, it is desirable to develop stable cathode interface layers (CILs) that can be processed over the photoactive layer using orthogonal solvents. In this study, an n-type naphthalene diimide core and oligo (ethylene glycol) side-chain-based conjugated polymer is reported as a universal, efficient CIL for organic and perovskite photovoltaics. Besides good thermal stability and easy processing in alcohol/water, the new CIL is found to possess electron transport properties with an electrical conductivity of 2.3 x 10(-6) S cm(-1), enabling its use as a CIL with a film thickness of up to similar to 35(+/- 2) nm. Utilizing the new CIL, 16% power conversion efficiency (PCE) is achieved for organic solar cells (OSCs) based on the PM6-Y6 photoactive layer (8.9% PCE for no CIL and 15.1% with state-of-the-art CIL, PDINO), and perovskite solar cells from methylammonium lead iodide yielded a PCE of 17.6%. Compared to the reference devices, the new CIL reduced trap-assisted carrier recombination and increased the built-in potential by 80 mV, simultaneously enhancing all photovoltaic parameters. Moreover, new CIL based devices had better photostability with no burn-in losses.