Study of neutron irradiation effects in Depleted CMOS detector structures
JOURNAL OF INSTRUMENTATION(2022)
摘要
In this paper the results of Edge-TCT and I-V measurements with passive test structures made in LFoundry 150 nm HV-CMOS process on p-type substrates with different initial resistivities ranging from 0.5 to 3 k Omega cm are presented. Samples were irradiated with reactor neutrons up to a fluence of 2.10(15) n(eq)/cm(2). The depletion depth was measured with Edge-TCT. The effective space charge concentration N-eff was estimated from the dependence of the depletion depth on bias voltage and studied as a function of neutron fluence. The dependence of N-eff on fluence changes with initial acceptor concentration in agreement with other measurements with p-type silicon. A long term accelerated annealing study of N-eff and detector current up to 1280 minutes at 60 degrees C was made. It was found that N-eff and current in reverse biased detector behave as expected for irradiated silicon.
更多查看译文
关键词
Particle tracking detectors (Solid-state detectors), Si microstrip and pad detectors, Solid state detectors
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要