N-Face Gan Substrate Roughening For Improved Performance Gan-On-Gan Led

Purpose This study aims to focus on roughening N-face (backside) GaN substrate prior to GaN-on-GaN light-emitting diode (LED) growth as an attempt to improve the LED performance. Design/methodology/approach The N-face of GaN substrate was roughened by three different etchants; ammonium hydroxide (NH4OH), a mixture of NH4OH and H2O2 (NH4OH: H2O2) and potassium hydroxide (KOH). Hexagonal pyramids were successfully formed on the surface when the substrate was subjected to the etching in all cases. Findings Under 30 min of etching, the highest density of pyramids was obtained by NH4OH: H2O2 etching, which was 5 x 10(9) cm(-2). The density by KOH and NH4OH etchings was 3.6 x 10(9) and 5 x 10(8) cm(-2), respectively. At standard operation of current density at 20 A/cm(2), the optical power and external quantum efficiency of the LED on the roughened GaN substrate by NH4OH: H2O2 were 12.3 mW and 22%, respectively, which are higher than its counterparts. Originality/value This study demonstrated NH4OH: H2O2 is a new etchant for roughening the N-face GaN substrate. The results showed that such etchant increased the density of the pyramids on the N-face GaN substrate, which subsequently resulted in higher optical power and external quantum efficiency to the LED as compared to KOH and NH4OH.