Controlled Magnetic Isolation And Decoupling Of Perpendicular Fept Films By Capping Ultrathin Cu(002) Nano-Islands

This study investigated the ultrathin Cu(002) capping nano-island effects on the magnetic characterizations and microstructure of epitaxial FePt(001) films directly fabricated on MgO(001) substrates at the relatively low temperature of 300 degrees C via electron-beam deposition. The enhancement of the coercivity is attributed to the lowered exchange coupling of FePt magnetic grains that begun from Cu atom behavior of spreading in many directions mainly along grain boundaries due to its lower surface energy than that of pure Fe or Pt. The measurement of angular-dependent coercivity shows a tendency of a domain-wall motion shift toward the rotation of the reverse-domain type upon the thickness of the Cu capping nano-island layer atop the FePt films. The intergranular interaction was clarified by the Kelly-Henkel plot, which indicated that there was strong exchange coupling (positive delta M) between neighboring grains in the FePt continuous films without Cu capping nano-islands. On the other hand, a negative delta M value was gained when the FePt films were capped with a Cu(002) single layer, indicating that the Cu capping layer can be used to control the strength of intergrain exchange coupling between the adjacent FePt grains and thicker Cu(002) capping nano-islands toward magnetic isolation; thus, there was an existence of dipole interaction in our designed Cu/FePt composite structure of stacked films.