The Effect Of Systematic Variation Of Ni:Co Ratio On The Oxidation Behaviour Of Gamma-Gamma ' Ni-Co-Al-Ti-Cr Alloys

The effect of Co:Ni ratio on the oxidation performance of gamma-gamma ' alloys based on the (Ni,Co)(75)Al5Ti5Cr15 system (at. %) was investigated. Seven model superalloys of Co concentration 0, 9, 19, 28, 38, 47 and 56 at.% underwent isothermal oxidation in air at 800 degrees C using both box-furnace exposure (1000 h) and thermogravimetric analysis (100 h). Following 1000 h oxidation at 800 degrees C, alloys containing 28, 38 and 47 at.% Co exhibited a flatter, more compact external scale and Cr2O3 layer as well as reduced oxygen ingress compared with alloys of lower Co content. The alloy containing 47 at.% Co exhibited two distinct morphologies.