Two-Dimensional Layered Nilip2s6 Crystals As An Efficient Bifunctional Electrocatalyst For Overall Water Splitting

The quest of earth-abundant bifunctional electrocatalysts for highly efficient oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) is essential for clean and renewable energy systems. Herein, directed by the experimental analysis, we demonstrate layered nickel lithium phosphosulfide (NiLiP2S6) crystal as a highly efficient water-splitting catalyst in alkaline media. With strained lattice due to stacked layers as observed by TEM and electronic structure analysis performed by XPS showed mixed Ni-2+,Ni-3+ oxidation states induced by addition of Li as a cation, NiLiP2S6 displays excellent OER (current density of 10 mA cm(-2) showed an overpotential of 303 mV vs. RHE and a Tafel slope of 114 mV dec(-1)) and HER activity (current density of -10 mA cm(-2) showed an overpotential of 184 mV vs. RHE and a Tafel slope of 94.5 mV dec(-1)). Finally, an alkaline media was employed to demonstrate the overall water splitting using NiLiP2S6 as both the anode and the cathode, which attained a 50 mA cm(-2) current density at 1.68 V. This bimetallic phosphosulfide, together with long-term stability and enhanced intrinsic activity, shows enormous potential in water splitting applications.