High Co Adsorption Performance Of Cucl-Modified Diatomites By Using The Novel Method "Atomic Implantation"

An atomic implantation method was used to modify diatomite with CuCl. The CuCl/diatomite samples were characterized by different techniques, including FTIR, XRD, BET, SEM-TEM, EDX, and CO-TPR. Characterization results revealed the formation of CuCl particles of 50-60 nm highly dispersed on diatomite surface. CO adsorption measurements showed that 2CuCl/diatomite exhibits the highest CO adsorption capacity among all CuCl-modified samples with diatomite. Its CO adsorption capacity of 2.96 mmol/g at 30 degrees C is 10 times higher than that of unmodified diatomite (0.29 mmol/g). The CO adsorption on CuCl-modified diatomites was found to fit well with the Langmuir-Freundlich model.