Immediate Soft-Tissue Adhesion And The Mechanical Properties Of The Ti-6al-4v Alloy After Long-Term Acid Treatment

Close attachment of soft tissues onto implantable devices inside the body is regarded as an optimal condition for preventing complications (e.g., infections and abscess formation around implants, and the migration of small injectable devices). We have recently reported that an alpha-type commercially pure Ti (CpTi) film after a long-term acid treatment and air drying showed a remarkable soft tissue adhesiveness immediately (i.e., within a few seconds) after the attachment onto soft tissues. Herein, we conducted acid treatment for (alpha + beta)-type Ti-6Al-4V alloys and compared their mechanical properties and the immediate soft-tissue adhesiveness with alpha-type CpTi. The acid treatment for Ti-6Al-4V also promoted immediate soft-tissue adhesion, although the treatment was less effective than for CpTi. The tensile strength of acid-treated Ti-6Al-4V was much higher than that of acid-treated CpTi or human skin tissues, although the degree of hydrogen embrittlement was more severe than that for CpTi. These results suggest that the small amount of Al in the major alpha phase and/or the minor beta phase of Ti-6Al-4V has a significant influence not only on the mechanical properties but also on the immediate soft-tissue adhesiveness of Ti-based solid-state adhesives after the acid treatment.