New Solvent And Coagulating Agent For Development Of Chitosan Fibers By Wet Spinning

Adipic acid was evaluated as a novel solvent for wet spinning of chitosan fibers. A solvent with two carboxyl groups could act as a physical crosslinker between the chitosan chains, resulting in improved properties of the fibers. The performance of adipic acid was compared with conventional solvents, i.e., lactic, citric, and acetic acids. Chitosan solutions were injected into a coagulation bath to form monofilaments. Sodium hydroxide (NaOH) and its mixture with ethanol (EtOH) were used as coagulation agents. Scanning electron microscopy confirmed the formation of uniform chitosan monofilaments with an even surface when using adipic acid as solvent. These monofilaments generally showed higher mechanical strength compared to that of monofilaments produced using conventional solvents. The highest Young's modulus, 4.45 GPa, was recorded for adipic acid monofilaments coagulated in NaOH-EtOH. This monofilament also had a high tensile strength of 147.9 MPa. Furthermore, taking advantage of chitosan insolubility in sulfuric acid (H2SO4) at room temperature, chitosan fibers were successfully formed upon coagulation in H2SO4-EtOH. The dewatering of fibers using EtOH before drying resulted in a larger fiber diameter and lower mechanical strength. Adipic acid fibers made without dehydration illustrated 18% (for NaOH), 46% (for NaOH-EtOH), and 91% (for H2SO4-EtOH) higher tensile strength compared to those made with dehydration.