Synergistic Effect Of Silane Cross-Linker (Apteos) On Pva/Gelatin Blend Films For Packaging Applications

The objective of this work is to fabricate hydrogel films which are biodegradable and also fit for packaging applications. The hydrogel films were prepared by the reaction of polyvinyl alcohol and gelatin with and without 3-aminopropyltriethoxysilane (APTEOS) cross-linker. The hydrogel films were then characterized by FTIR spectroscopy, degree of swelling, TGA, SEM analysis and mechanical testing. The FTIR spectra of the hydrogel films confirmed the presence of both polymers and hydrogen bonding between them. TGA analysis confirmed the increase in thermal stability with the increase of cross-linker amount. SEM analysis confirmed the increase in uniformity of structure with the increase of cross-linker amount. The increase in cross-linker amount resulted in decrease of degree of swelling and increase of tensile strength. The biodegradability of hydrogel films was evaluated by performing soil burial test and found to be decreased with the increase of cross-linker amount. In order to balance the tensile strength and biodegradability, the optimum amount of cross-linker was determined which resulted in the formation of the best performing film. Finally, our best performing film was compared with other hydrogel films reported in the literature. Hence, the hydrogel films cross-linked with APTEOS are biodegradable, having high tensile strength and suitable for packaging purpose.