Instability Of In Situ Tic Particles In An Al-12si Alloy
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T(2020)
摘要
This paper studied the evolution of in situ TiC particles in an Al-12Si alloy and the effect of Si on their stability. The samples were observed with scanning electron microscopy, and the phase analysis was performed by energy dispersive spectroscopy, X-ray diffraction, and transmission electron microscopy. The results demonstrated that Si can directly promote the evolution of TiC. After holding the TiC/Al-12Si alloy (TiC content of 2.75 wt.%) at 800 degrees C for 5 min, a large amount of TiC reacted with Al to form an Al4C3 phase and the Ti in TiC reacted with Al and Si to form a TiAlSi phase. When the holding time was increased to 20 min, the TiC almost completely disappeared. The morphology of TiC gradually changed from a regular tetra-decahedron to a sphere when Si was not added, and the average size gradually decreased from 1 mu m and eventually disappeared completely. Si can diffuse into the TiC lattice to destroy its structure, thus forming a Si-rich disordered layer at the edge of the TiC particles. The values of diffusion resistance of Ti and C atoms in TiC, decrease owing to the destruction of the TiC lattice structure, which accelerates the TiC transformation reaction. (C) 2020 Published by Elsevier B.V.
更多查看译文
关键词
TiC, Instability, Al-12Si alloy, Al4C3, Lattice structure
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要