Rejuvenation through plastic deformation of a La-based metallic glass measured by fast-scanning calorimetry

We explore the glassy states achievable after a metallic glass is formed on liquid quenching. Samples of La55Al25Ni20 (at.%) metallic glass (rod and ribbon) are studied. The extent of structural relaxation at room temperature is characterized for this low-glass-transition temperature glass. Plastic deformation (uniaxial compression) rejuvenates the glass to states of higher enthalpy characteristic of glass formation at high cooling rate. Deformation increases the heterogeneity of the glass, widening the spectrum of relaxation times. The extent of rejuvenation in samples of low aspect ratio is compared with that under conditions of high constraint in notched samples. The deformation-induced rejuvenation is particularly susceptible to reduction on subsequent ageing. Fast-scanning calorimetry is useful in characterizing the dynamics of structural relaxation. The shadow glass transition is more evident on fast heating, and is observed in this glass for the first time. A new excess exothermic effect is observed before the glass transition.