Biosourced All-Acrylic Aba Block Copolymers With Lactic Acid-Based Soft Phase

Lactic acid is one of the key biobased chemical building blocks, given its readily availability from sugars through fermentation and facile conversion into a range of important chemical intermediates and polymers. Herein, well-defined rubbery polymers derived from butyl lactate solvent were successfully prepared by reversible addition-fragmentation chain transfer (RAFT) polymerization of the corresponding monomeric acrylic derivative. Good control over molecular weight and molecular weight distribution was achieved in bulk using either monofunctional or bifunctional trithiocarbonate-type chain transfer agents. Subsequently, poly(butyl lactate acrylate), with a relative low T-g (-20 degrees C), good thermal stability (5% wt. loss at 340 degrees C) and low toxicity was evaluated as a sustainable middle block in all-acrylic ABA copolymers using isosorbide and vanillin-derived glassy polyacrylates as representative end blocks. Thermal, morphological and mechanical properties of copolymers containing hard segment contents of <20 wt% were evaluated to demonstrate the suitability of rubbery poly(alkyl lactate) building blocks for developing functional sustainable materials. Noteworthy, 180 degrees peel adhesion measurements showed that the synthesized biosourced all-acrylic ABA copolymers possess competitive performance when compared with commercial pressure-sensitive tapes.