Microwave Synthesis of Co–Ni Ferrite/Graphene Nanocomposite for Microwave Absorption

As the absorbing material composed of sole carbon is difficult to meet the comprehensive requirements of microwave applications, preparation of carbonaceous nanocomposite materials becomes an effective method to increase microwave absorption properties. In this study, a novel nanocomposite composed of Co–Ni ferrite and graphene was synthesized via a simple and rapid microwave hydrothermal method in just a few minutes. It was demonstrated that the minimum microwave reflection loss of the composite of 3 mm thickness with a low filling ratio (20 wt%) reached −13.1 dB at 17.2 GHz with an effective absorption bandwidth of 3.1 GHz. The good performance of the composite was believed to be a result of high dielectric loss of graphene associated with a multi-dielectric relaxation process and magnetic loss of the ferrite mainly originated from natural ferromagnetic resonance.