Adhesive agent for injection molding of aluminum nitride ceramic and application method of adhesive agent

The invention belongs to the technical field of ceramic material preparation and discloses an adhesive agent for injection molding of aluminum nitride ceramic and an application method of the adhesive agent. The adhesive agent comprises the following ingredients: 50-70% of microcrystalline wax, 25-40% of high polymer, 3-10% of surface modifier and 2-12% of resin. The application method of the adhesive agent comprises the following steps of mixing aluminum nitride powder and the adhesive agent, putting in a mixing mill for heating and mixing to prepare a feed, carrying out the injection molding to prepare a green body, preparing a degreased blank after degreasing, carrying out high-temperature sintering at last to form a finish product. In a sintering process, heat preservation is carried out at a specific temperature point to achieve carbon thermal reduction to further reduce an oxygen content, and then the temperature is raised to the maximum temperature for sintering and compacting. The adhesive agent has excellent liquidity and shape preserving property, and a specific carbon residue rate after thermal degreasing, and the aluminum nitride ceramic prepared by the adhesive agent has upper heat conductivity.