Mussel-Inspired Approach to Constructing Dual Network Coated Layered Clay for Enhanced Barrier and Antibacterial Properties of Poly(vinyl alcohol) Nanocomposites.

Inspired by complexation and mussel adhesion of catechol groups in tannic acid (TA), organophilic layered double hydroxides (LDHs@TA-Ti) were synthesized by forming a one-pot assembled TA-titanium (Ti) dual network coating on the surface of layered clay for the first time. LDHs@TA-Ti/poly(vinyl alcohol) (PVA) nanocomposites were prepared by the solution casting method. The results show that TA-Ti(IV) and TiO2 coordination compounds are simultaneously formed due to hydrolysis of titanium tetrachloride and complexation of TA in aqueous solution. Upon TA-Ti coatings onto the surface of LDHs, the antibacterial rate of LDHs@TA-Ti is up to 99.98%. Corresponding LDHs@TA-Ti/PVA nanocomposites also show outstanding antibacterial properties. Compared with pure PVA, LDHs@TA-Ti/PVA nanocomposites show a 40.9% increase in tensile strength, a 17.5% increase in elongation at break, a 35.9% decrease in oxygen permeability and a 26.0% decrease in water vapor permeability when adding 1 wt % LDHs@TA-Ti. UV transmittance (at 300 nm) of LDHs@TA-Ti/PVA nanocomposites decrease by 99.4% when the content of LDHs@TA-Ti reaches 3 wt %. These results indicate that PVA matrix incorporated with LDHs@TA-Ti could be used as a potential active packaging material to extend the shelf life of food products.