Bright and Uniform Green Light Emitting InP/ZnSe/ZnS Quantum Dots for Wide Color Gamut Displays

ACS APPLIED NANO MATERIALS(2019)

引用 168|浏览11
暂无评分
摘要
There is an urgent demand to improve the efficiency and the color purity of the environment-friendly quantum dots (QDs), which can be used in wide color gamut (WCG) displays. In this study, we optimized the reaction conditions for the InP core synthesis and the ZnSe/ZnS multishell growth on the core. As a result, remarkable improvements were achieved in the photoluminescence quantum yield (PL QY, 95%) and the full width at half maximum (fwhm, 36 nm), with perfectly matched wavelength (528 nm) for the green color in WCG displays. Injection of the phosphorus precursor at a mild temperature during the InP core synthesis reduced the size distribution of the core to 12%, and the shell growth performed at a high temperature significantly enhanced the crystallinity of the thick passivating layer. We also investigated the photophysical properties, particularly the energy trap distributions and trap state emissions of the InP-based QDs with different shell structures. The time-resolved and temperature-dependent PL spectra clearly indicated that the wellpassivated InP/ZnSe/ZnS QDs showed nearly trap-free emissions over a wide temperature range (77-297 K). Also, the on and off-time probability on single QD blinking and Auger ionization efficiencies also showed that these QDs were hardly affected by the surface traps.
更多
查看译文
关键词
quantum dots,indium phosphide,multishell,photoluminescence,trapping rate,blinking suppression,Auger ionization efficiency
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要