In vitro cyclic fatigue and hydrothermal aging lifetime assessment of yttria-stabilized zirconia dental ceramics
Journal of the European Ceramic Society(2020)
摘要
The in vitro lifetime assessment of dental zirconia has been the focus of researchers. This work mainly studied the cyclic fatigue lifetime in saliva and aging lifetime of three commercial zirconia dental materials: two kinds of 3 mol%-yttria stabilized zirconia ST(super-translucence) and MT(medium-translucence), in which MT contains a small amount of alumina; a 5 mol%-yttria stabilized zirconia TT(tooth-translucency). ST and MT materials have higher initial mechanical strength (flexural strength) and initial crack propagation threshold than TT materials, thus they have longer cycle fatigue lifetime, but TT has best aging resistance(no aging) in existing aging procedures. MT has a higher initial mechanical strength and better aging resistance than ST samples due to the influence of alumina at grain boundary, but has lower strength reliability. Finally the service lifetime of the three materials was evaluated, and some guidance for their use is provided.
更多查看译文
关键词
Zirconia,Aging,Cycle fatigue
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络