Functionalized Multiarmed Polycaprolactones as Biocompatible Tissue Adhesives.

Existing tissue adhesives have a trade-off between adhesive strength and biocompatibility. Here, we report a series of biocompatible multiarmed polycaprolactones (PCL) as tissue adhesives that can be released from a hot glue gun and the length of each arm was kept at ∼2-3 kg mol in all the polymers. The adhesion properties were dependent on the number of functionalized (-hydroxysuccinimide ester (NHS), aldehyde (CHO), and isocyanate (NCO)) arms of the multiarmed polymers. The more arms, the higher the adhesion strength. For example, the adhesion strength in binding cut rat skin increased from 2.3 N cm for 2PCL-NHS to 11.2 N cm for 8-PCL-NHS. CHO- and NCO-modified 8PCL also had suitable adhesive properties. All the multiarmed polymers had minimal cytotoxicity and good biocompatibility , suggesting their potential as promising alternative surgical adhesives.