High Purity and Low Molecular Weight Lignin Nano-Particles Extracted from Acid-Assisted MIBK Pretreatment.

A simple and economical biorefinery method, organosolv methyl isobutyl ketone (MIBK) pretreatment assisted by Lewis acid ferric trichloride hydrolysis, was proposed for fractionating the lignin from extractive-free Eucalyptus powder at the nanoscale, accompanied by another product furfural, derived from hemicellulose. Under the conditions (180 degrees C, 1 h) optimized based on the best yield of furfural, 40.13% of the acid-insoluble lignin (AIL) could be obtained with a high purity of 100%, a low molecular weight of 767 (M-n) and improved thermostability. The extracted lignin was characterized by its chemical structure, thermostability, homogeneity, molecular weight, and morphology as compared with milled wood lignin (MWL). The results showed significant variations in chemical structures of the extracted lignin during the pretreatment. Specifically, the aryl ether linkage and phenylcoumarans were broken severely while the resinols were more resistant. The G-type lignin was more sensitive to degradation than the S-type, and after the pretreatment, H-type lignin was formed, indicating the occurrence of a demethoxylation reaction at high temperature. Moreover, the lignin nano-particles were identified visually by AFM and TEM images. The dynamic light scattering (DLS) showed that the average diameter of the measured samples was 131.8 nm, with the polydispersity index (PDI) of 0.149. The MIBK-lignin nano-particles prepared in our laboratory exhibit high potentials in producing high functional and valuable materials for the application in wide fields.