Corrosion behaviour of thermally sprayed Mo added AlCoCrNi high entropy alloy coating

AlCoCrNi alloy was modified by adding Mo to increase its corrosion resistance. Mo was successfully added to the alloy using mechanical milling. All the five constituents of the alloy were milled in a high-energy planetary ball-mill for 20 h. The effective concentration of Mo in the alloy was 10%. At equal intervals, samples were taken for phase formation studies using X-ray diffractional analysis (XRD). The micro-structural characterization was carried out to confirm the homogeneity of the alloy using Field emission scanning electron microscopy (FESEM). The resultant high entropy alloy (HEA) powder was thermally sprayed over a 316l substrate using High-velocity Oxy-fuel (HVOF) technique. Corrosion characteristics of the coating were studied using potentio-dynamic polarization (PDP) test under standard condition. The corrosion properties of the coating were compared with conventional NiCrSiB corrosion resistant coating. The AlCoCrMoNi HEA system offers better resistance to corrosion than NiCrSiB coating.