A study of corrosion enhanced erosion in Nickel Aluminium Bronze with Niobium and Yttrium

An investigation was carried in Nickel Aluminium Bronze (NAB) alloyed with Niobium (Nb) and Yttrium (Y) to study the effect of the microstructure for onshore applications. Nickel Aluminium Bronze is broadly used in aqueous atmospheres due to their good mechanical and corrosion resistance properties. The presence of destructive species in aqueous water initiates the corrosion of the engineering modules is inevitable. In -order to optimize the corrosion resistance Nb and Y were added as (1%, 2% & 3%) respec- tively in the master NAB. The specimens were exposed to the immersion test in NaCl solution. To create the behavior of corrosion and succeeding erosion, altered immersions hours were selected as 8, 16, 24, 32, 40, 48 and 54 h. The mass loss measurements were obtained after the completion of the individual spec- ified time to calculate corrosion rates (CR). Solid particle erosion (SPE) investigations were also carried out on the developed alloys. The size of the particle which is used in the investigation is 50 mm. Corrosion rate was calculated and it is correlated with the immersion time. Scanning electron microscopy (SEM) investigations were observed for the corroded and eroded specimens. (C) 2019 Elsevier Ltd. All rights reserved. Selection and peer -review under responsibility of the scientific committee of the International conference on Materials and Manufacturing Methods.