Characterizing temperature-dependent optical properties of (MA 0.13 FA 0.87 ) PbI 3 single crystals using spectroscopic ellipsometry

In this paper, we present spectroscopic ellipsometry measurements of (MA 0.13 FA 0.87 )PbI 3 single crystals assessed at photon energies of 0.73–6.42 eV and at temperatures between 4.4 and 400 K. At room temperature, the refractive index was dispersed as a function of frequency, which is typical of a semiconductor. The absorption spectrum exhibited several electronic transitions. We estimated a room temperature direct band gap of 1.66 ± 0.02 eV and exciton binding energy of 40 meV. With decreasing temperature, the refractive index increased. The room-temperature thermo-optic coefficients were −1.7 × 10 −4 and −2.5 × 10 −4 K −1 at wavelength of 600 and 1200 nm. The exciton peak position and bandgap energy exhibited a redshift, which was attributed to a reverse ordering of the band structures. Additionally, an anomaly in exciton peak position and bandgap occurred at approximately 100–200 K due to the structural phase transition. This phenomenon was associated with the coexistence of MA/FA-disordered and MA/FA-ordered domains. Our results provide a foundation for the technological development of lead halide perovskites-based photonic devices at various temperatures.