Magnetic Behavior of Carbon Materials Made from Biomass by Fe-Assisted Hydrothermal Carbonization.

Biomass magnetic materials were synthesized by several hydrothermal carbonization methods, by which iron was provided in different ways: as FeCl3 prior to or during hydrothermal carbonization, as pure Fe particles, or as magnetic ferrofluid, followed or not by pyrolysis processes. The materials were thoughtfully characterized in terms of elemental composition, thermal degradation, porosity (N-2 adsorption, SEM micrography), surface chemistry (FTIR spectroscopy, XRD diffraction), and magnetization curves on a self-made installation. The results indicated that the process design can significantly improve the structure and chemistry of the material, as well as the magnetization effect induced on the adsorbent. Fe as FeCl3 was more interesting in regards to the development of porosity, mainly creating micropores, although it did not provide magnetism to the material unless a further pyrolysis was applied. Thermal treatment at 600 degrees C did not only increase the BET-specific surface (S-BET) (262 m(2) g(-1)) of the hydrochar, but also involved the transformation of Fe into magnetite, providing magnetic behavior of the hydrochar. Increasing pyrolyisis temperature to 800 degrees C even enhanced a better development of porosity (S-BET of 424 m(2) g(-1)) and also increased the specific magnetic susceptibility of the hydrochar as a result of the further transition of Fe into wustite and hydroxi-ferrite.