A natural energy absorbent polymer composite: The equine hoof wall.

The equine hoof has been considered as an efficient energy absorption layer that protects the skeletal elements from impact when galloping. In the present study, the hierarchical structure of a fresh equine hoof wall and the energy absorption mechanisms are investigated. Tubules are found embedded in the intertubular matrix forming the hoof wall at the microscale. Both tubules and intertubular areas consist of keratin cells, in which keratin crystalline intermediate filaments (IFs) and amorphous keratin fill the cytoskeletons. Cell sizes, shapes and IF fractions are different between tubular and intertubular regions. The structural differences between tubular and intertubular areas are correlated to the mechanical behavior of this material tested in dry, fresh and fully hydrated conditions. The stiffness and hardness in the tubule areas are higher than that in the intertubular areas in the dry and fresh samples when loaded along the hoof wall; however, once the samples are fully hydrated, the intertubular areas become stiffer than the tubular areas due to higher water absorption in these regions. The compression behavior of hoof in different loading speed and directions are also examined, with the isotropy and strain-rate dependence of mechanical properties documented. In the hoof walls, mechanistically the tubules serve as a reinforcement, which act to support the entire wall and prevent catastrophic failure under compression and impact loading. Elastic buckling and cracking of the tubules are observed after compression along the hoof wall, and no shear-banding or severe cracks are found in the intertubular areas even after 60% compression, indicating the highly efficient energy absorption properties, without failure, of the hoof wall structure.