Enhanced Properties Of Poly(Styrene-B-Ethylene-Co-Butylene-B-Styrene) Nanocomposites With In Situ Construction Of Interconnected Graphene Network
JOURNAL OF APPLIED POLYMER SCIENCE(2019)
摘要
In this work, such elastomeric nanocomposites were fabricated with graphene (GE) sheets selectively distributing between polymer matrices and forming three-dimensional networks. The solvent evaporation process was first introduced to produce poly(styrene-ethylene-co-butadiene-b-styrene) (SEBS) microspheres and then reduced GE oxide attached to the surface of SEBS microspheres via electrostatic interaction and sonication-assisted reduction. The microstructure of nanocomposites, prepared by compression molding using SEBS/GE microspheres, was investigated using scanning electron microscopy and transmission electron microscopy. The results showed that interconnected GE networks formed in heat-pressing composite and was destroyed after twin-roll mixing. The SEBS/GE nanocomposites showed enhanced electrical, thermal, and mechanical properties. The electrical resistivity of nanocomposites obtained via heat-pressing reached to 1.1x10(3)m at a 2.5 wt % (1.07vol %) content of GE. The thermal and mechanical properties were also characterized. It was found that the initial degradation temperature increased by nearly 40 degrees C and the mechanical properties continued to rise with GE content below 0.5 wt %. (c) 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 47118.
更多查看译文
关键词
composites, elastomers, graphene
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要