Microstructure, dielectric, piezoelectric, and ferroelectric properties of fine-grained 0.94Na0.5Bi0.5TiO3-0.06BaTiO3 ceramics

For preparing fine-grained 0.94Na0.5Bi0.5TiO3-0.06BaTiO3 lead-free ferroelectric ceramics, the precursor powders were synthesized via sol-gel method and calcined at various temperatures. The precursor powders calcined at 520 °C, 550 °C, and 600 °C exhibit mean grain sizes of 30 ± 4 nm, 54 ± 3 nm, and 78 ± 5 nm, respectively. By optimizing the synthesis parameters, the fine-grained ceramics with high relative densities (>97%) and mean grain size around 100 nm were prepared. The ferroelectric, dielectric, and piezoelectric behavior were investigated. The ceramics prepared using the different precursor powders show different piezoelectric, ferroelectric, and dielectric behavior. The ceramic calcined at 550 °C and sintered at 900 °C exhibits the breakdown strength higher than 85 kV/cm, which exhibits the maximum polarization of 38.4 ± 0.3 μC/cm2, remanent polarization of 20.6 ± 0.4 μC/cm2.