Fabrication and kW-level MOPA laser output of planar waveguide YAG/Yb:YAG/YAG ceramic slab

Using the tape casting method combined with vacuum sintering and hot isostatic pressing, high-quality planar waveguide YAG/10at.%Yb:YAG/YAG ceramics were successfully prepared. For the sample presintered at 1750 degrees C for 30hours and then HIPed at 1700 degrees C for 3hours in 200 MPa argon, the in-line transmittance reached 82.5% at 400nm and the average grain size was similar to 17.1m. The diffusion behaviors of Yb ions across the contact boundary between the cladding YAG layer and the core Yb:YAG layer were determined by Fick's second law. Then, a 1030nm continuous-wave (CW) Yb:YAG planar waveguide ceramic laser based on the structure of master oscillator power amplification (MOPA) was realized. After a single-pass amplification, the maximum output of the ceramic slab (60x10x1mm(3)) reached 1251W and the corresponding optical-to-optical efficiency was 30.0%, which is the highest output power of a Yb:YAG planar waveguide ceramic laser to the best of our knowledge.