A novel route for the synthesis of ultrafine WC-15 wt %Co cemented carbides

In this study, a solution chemical route for the synthesis of ultrafine WC-15 wt %Co cemented carbides was proposed with WC-6Co aggregates as raw materials. The chemical Co was uniformly distributed around the WC-6Co aggregates and the Co layers in the raw materials had been well preserved. During sintering, the chemical Co could diffuse along the Co layers and thus avoid the aggregation and growth of WC grains. Additionally, the homogeneous distribution of Co phase and the existent of Co layers promoted the WC reprecipitations on the same crystal during the solution/re-precipitation process. The fine WC grains and the homogeneous of WC and Co phases resulted in the high hardness and transverse rupture strength.