Hot ductility of high Al TWIP steels containing Nb and Nb-V

The hot ductility of B-Ti-Nb-high Al (1.5%Al) containing TWIP steels having Ti/N ratios mainly in excess of 3.4/1 was obtained. After soaking at 1250 degrees C, the tensile specimens were cooled at 12 or 60 degrees Cmin(-1) to the test temperature and then strained to failure at 3x10(-3)s(-1). Ductility was always good (reduction of area >40%), independent of Ti/N ratio or cooling rate. The good ductility is due to B segregation strengthening the grain boundaries and the low S level (0.005%S) limiting the volume fraction of MnS inclusions and restricting AlN precipitation to the matrix. Increasing the cooling rate, higher N levels and Nb resulted in a small improvement in ductility. An addition of V to the Nb-containing steels caused a slight deterioration in the hot ductility.