Visible and near-infrared luminescent properties of Pr3+ doped strontium molybdate thin films by a facile polymer-assisted deposition process.

Quartz substrate supported Praseodymium (Pr) doped strontium molybdate (SrMoO4) thin films with good uniformity and outstanding fluorescent properties are successfully fabricated via a facile polymer-assisted deposition (PAD) method. In combination with the strong chelating effect of water-soluble polymer on metal cations, the free cations without chelating are effectively ruled out but the remaining chelating metal cations are employed for the highly uniform and accurate stoichiometry luminescent SrMoO4: Pr thin films, layer-by-layer mounting on the common quartz substrates. More importantly, the excellent release of stress from polymer during the growth process of epitaxial thin film can effectively overcome the mismatch between thin film and common quartz substrate and then guarantee the quality of thin film. Under the ultraviolet (UV) light excitation, the samples show high luminescence intensity both in visible and near-infrared (NIR) regions peaked at 646 nm and 1037 nm, mainly ascribing to the transitions of 3P0 → 3F2 and 1G4 → 3H4 of Pr3+ ions. The luminescent properties can be tailored by optimizing the number of spin-coated layers and doping concentrations. The maximum emission occurs at 4 mol% of Pr3+ dopant, and it exhibits an impressive high photoluminescence quantum yield (QY) of up to 86.12%. These results evidently demonstrate the present PAD method is a useful prototype for preparing high performance luminescent thin films even on the cheap quartz substrate.