Preparation of network-like ZnO–FeWO4 mesoporous heterojunctions with tunable band gaps and their enhanced visible light photocatalytic performance

NEW JOURNAL OF CHEMISTRY(2015)

引用 39|浏览2
暂无评分
摘要
Novel mesoporous ZnO-FeWO4 (Zn-FeWO4) heterojunctions with network-like structure were synthesized with a combination of thermal decomposition and hydrothermal methods. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), N-2 sorption and Brunauer-Emmett-Teller (BET) surface area analysis, diffuse reflection spectroscopy (DRS) and photoluminescence spectroscopy (PL). The results showed that the size of FeWO4 was reduced by the modification of ZnO. With the increasing molar ratio of ZnO to FeWO4, the quantum size of FeWO4 decreased from 11 nmto 4 nm, as is followed by a surprisingly band gap broadening. Photocatalytic activity toward the degradation of RhB under visible light irradiation was investigated. The optimum decomposition rate of RhB using the prepared 1.5Zn-FeWO4 heterojunction was almost 39 and 9.7 times that of pristine ZnO and FeWO4, respectively. The active species trapping experiments showed that the holes exhibited an obvious influence on the photocatalytic degradation process. The study on the mechanism showed that the enhanced photocatalytic activity was mainly ascribed to heterojunction construction and band gap broadening, which enhance the efficient transfer and the oxidation potential of holes. This heterojunction shows a potential industrial application to remove undesirable organics from the environment.
更多
查看译文
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要