Thermophysical properties of americium-containing barium plutonate

Polycrystalline specimens of americium-containing barium plutonate have been prepared by mixing the appropriate amounts of (Pu0.91Am0.09)O-2 and BaCO3 powders followed by reacting and sintering at 1600 K under the flowing gas atmosphere of dry-air. The sintered specimens had a single phase of orthorhombic perovskite structure and were crack-free. Elastic moduli were determined from longitudinal and shear sound velocities. Debye temperature was also determined from sound velocities and lattice parameter measurements. Thermal conductivity was calculated from measured density at room temperature, literature values of heat capacity and thermal diffusivity measured by laser flash method in vacuum. Thermal conductivity of americium-containing barium plutonate was roughly independent of temperature and registered almost the same magnitude as that of BaPuO3 and BaUO3.