Defect Generation Mechanisms in PVT-Grown AlN Single Crystal Boules

A systematic study on the density and distribution of extended defects in a typical single crystal AlN boule grown by the physical vapor transport (PVT) method has been carried out in order to gain a detailed understanding of the formation of defects such as dislocations and low angle grain boundaries (LAGBs). Boule surface studies reveal that LAGBs are nucleated during initial stages of growth and propagate to the end of growth. Basal plane dislocations (BPDs) are generated during growth due to thermal gradient stresses. Higher BPD densities are found near the LAGBs at the boule edges due to additional stresses from constrained growth. Threading edge dislocations (TEDs) are typically replicated from the seed, and LAGBs composed of arrays of threading dislocation walls are formed to accommodate the c-axis rotation between different groups of threading screw dislocation (TSD) mediated growth centers.