Effect of Tempering and Baking on the Charpy Impact Energy of Hydrogen-Charged 4340 Steel
Journal of Materials Engineering and Performance(2014)
摘要
Tempered AISI 4340 steel was hydrogen charged and tested for impact energy. It was found that samples tempered above 468 °C (875 °F) and subjected to hydrogen charging exhibited lower impact energy values when compared to uncharged samples. No significant difference between charged and uncharged samples tempered below 468 °C (875 °F) was observed. Neither exposure nor bake time had any significant effect on impact energy within the tested ranges.
更多查看译文
关键词
4340 steel, baking, charpy impact test, hydrogen charging