Triethanolamine – solution for rapid hydrothermalsynthesis of titanate nanotubes

Titanate nanotubes were prepared by a rapid hydrothermal method in the presence of triethanolamine (TEA) using TiO2 nanoparticles as a precursor. The addition of TEA significantly reduced the formation time of the titanate nanotubes from 24 to 6 h. The crystalline structure of the titanate nanotubes was revealed to be H2Ti2O5 through the X-ray diffraction (XRD) measurement. The morphology of the titanate nanotubes was confirmed using transmission electron microscopy (TEM) while the surface area was characterized using Brunauer-Emmett-Teller (BET) surface area analysis. The titanate nanotubes produced were several hundred nanometers in length and had an average outer diameter of similar to 11.5 nm, inner diameter of similar to 5.0 nm, interlayer spacing of 0.93 nm and surface area of >250 m(2)/g. The photocatalytic activity of the titanate nanotubes was studied using methylene blue as a model dye; the titanate nanotubes showed better photocatalytic performance as compared to TiO2 nanoparticles.